NYLAFORCE® B 50 Z SCHWARZ
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LEIS Polytechnik - polymere Werkstoffe GmbH |
| Trademark: | NYLAFORCE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | apa8vM_NYLAFORCE-B-50-Z-SCHWARZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| produced by feed up-process, polyamide 6 + 50% glass fibres, heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.56 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.10 to 0.50 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C 1 | -- | 11500 | MPa | |
| 23°C | 16500 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| 23°C 2 | -- | 150 | MPa | |
| 23°C | 220 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, 23°C 3 | -- | 5.0 | % | |
| Break, 23°C | 2.6 | -- | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -- | 14 | -- | kJ/m² | |
| 23°C 4 | -- | 26 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -- | 85 | -- | kJ/m² | |
| 23°C 5 | -- | 86 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 6 | 221 | -- | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Testing according to ISO 527ISO 1110 |
| 2 . | Testing according to ISO 527ISO 1110 |
| 3 . | Testing according to ISO 527ISO 1110 |
| 4 . | Testing according to ISO 179ISO 1110 |
| 5 . | Testing according to ISO 179ISO 1110 |
| 6 . | 10K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® N 2320 0035 LEV | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| DOW™ LDPE PG 7004 (Extrusion Coating) | The Dow Chemical Company | LDPE | DOW™ LDPE |
| Multiuse Leostomer® LJ-3160N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| apilon 52c® C 61HV | API SpA | TPU-Polyester | apilon 52c® |
| Plaslube® PA6/6 GF10 TL5 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |