XENOY™ X4830 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | apPdNw_XENOY-X4830-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XENOY X4830 is a hydrostable, high modulus, low temperature ductile PC/PBT blend. Furthermore, this resin provides high chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional stability. The X4830 could be positioned for body panels, safety equipment, housings, doorhandles, spring-loaded applications, medical device enclosures, outdoor sports equipment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (266°C/5.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 0.90 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.42 | % | |
| Equilibrium, 23°C, 50% RH | 0.14 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 105 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3400 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 56.0 | MPa | ASTM D638 |
| Yield 3 | 60.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Yield | 61.0 | MPa | ISO 527-2/50 |
| Break 4 | 60.0 | MPa | ASTM D638 |
| Break 5 | 60.0 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/5 |
| Break | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 6 | 4.5 | % | ASTM D638 |
| Yield 7 | 4.1 | % | ASTM D638 |
| Yield | 4.1 | % | ISO 527-2/5 |
| Yield | 4.2 | % | ISO 527-2/50 |
| Break 8 | 150 | % | ASTM D638 |
| Break 9 | 140 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/5 |
| Break | 110 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 10 | 3100 | MPa | ASTM D790 |
| -- 11 | 2900 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 12 | 96.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 30.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 13 | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Charpy Unnotched Impact Strength 14 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 120 | J/m | ASTM D256 |
| 0°C | 150 | J/m | ASTM D256 |
| 23°C | 600 | J/m | ASTM D256 |
| -30°C 15 | 9.0 | kJ/m² | ISO 180/1A |
| 0°C 16 | 15 | kJ/m² | ISO 180/1A |
| 23°C 17 | 45 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 18 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact | |||
| -20°C, Total Energy | 70.0 | J | ASTM D3763 |
| 23°C, Total Energy | 70.0 | J | ASTM D3763 |
| -- | 110 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 125 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 19 | 119 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 106 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 20 | 97.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 133 | °C | ASTM D1525, ISO 306/B50 11 21 |
| -- | 135 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : -30 to 80°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 8.2E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -30 to 80°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 240 to 265 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 255 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 50 mm/min |
| 8 . | Type I, 5.0 mm/min |
| 9 . | Type I, 50 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2.0 mm/min |
| 12 . | 1.3 mm/min |
| 13 . | 80*10*4 sp=62mm |
| 14 . | 80*10*4 sp=62mm |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 |
| 19 . | 80*10*4 mm |
| 20 . | 80*10*4 mm |
| 21 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB25-501 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Sinvicomp SGH5500G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Amodel® AS-1933 HS | Solvay Specialty Polymers | PPA | Amodel® |
| Hyundai EP PA6 LS950 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| LUVOCOM® 80-8444 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |