KOPA® KN120
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | apBFvY_KOPAKN120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPA®KN120 is a polyamide 6 (nylon 6) product,. It is available in North America, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.3 - 1.5 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 1.8 | % | ASTM D570 |
| Comonomer Content | < 0.8 | % | |
| Color b | -3.80 - 0.200 | ||
| Color L | 70.0 - 78.0 | ||
| Moisture Content | % | ||
| Relative viscosity- 96% h2s04 | 2.61 - 2.69 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Amino End Groups | 43 - 63 | meq/kg |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 81.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 100 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2750 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 123 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 74 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 180 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.0 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tygothane C-210-A | Saint Gobain - Norton | PUR-Ester | Tygothane |
| Multiuse Leostomer® LJ-3170N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| DINALON® PA 6.6 30% FV | Grupo Repol | Nylon 66 | DINALON® |
| Karina BLUE PVC COMPOUND 900D06/469-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |