Zytel® ST801A NC010A
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ap9Ew0_ZytelST801ANC010A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced, Super Toughened, Polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.07 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.4 | -- | % | ISO 294-4 |
| Flow | 1.8 | -- | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | 900 | MPa | ISO 527-2 |
| Tensile Stress (50% Strain) | 49.0 | 44.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | > 50 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 800 | MPa | ISO 899-1 |
| 1000 hr | -- | 700 | MPa | ISO 899-1 |
| Flexural Modulus | 1800 | 700 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 20 | 20 | kJ/m² | ISO 179/1eA |
| 23°C, local fracture | 70 | 100 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 20 | 17 | kJ/m² | ISO 180/1A |
| -30°C | 15 | 15 | kJ/m² | ISO 180/1A |
| 23°C | 80 | 90 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 157 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 63.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 75.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 205 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ||||
| Flow : 23 to 55°C | 1.4E-4 | -- | cm/cm/°C | ASTM E831 |
| Flow | 1.4E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flow : -40 to 23°C | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flow : 55 to 160°C | 1.6E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.3E-4 | -- | cm/cm/°C | ASTM E831 |
| Lateral | 1.3E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Horizontal : -40 to 23°C | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Horizontal : 55 to 160°C | 1.3E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 8.7E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | 25 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.50 | 5.90 | IEC 60250 | |
| 1 MHz | 3.30 | 3.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.0E-3 | 0.16 | IEC 60250 | |
| 1 MHz | 0.010 | 0.038 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.8 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| Oxygen Index | 20 | -- | % | ISO 4589-2 |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 290 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 300 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Ejection Temperature | 190 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 100 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Seblex® 7850 | PolyPacific Pty. Ltd. | Rubber | Seblex® |
| Wondel® T PETG6 | Nanjing Julong Engineering Plastics Co., LTD | PET | Wondel® T |
| LUVOCOM® 1105-8000 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| POLYCOMPO PP J707EG | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |
| PENTAMID A S GV25 H FR natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |