Kangxi® 6515HP-NHV0
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Wuxi Kangxi Plastics Technology Co.,Ltd. |
| Trademark: | Kangxi® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aorulg_Kangxi6515HPNHV0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kangxi®6515HP-NHV0 is a polyphenylene ether PS (PPE PS) product,. It can be processed by injection molding and is available in the Asia-Pacific region. Kangxi®Application areas of 6515HP-NHV0 include electrical/electronic applications and housing. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | 57.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 4 | 2000 | MPa | ASTM D790 |
| Flexural Strength 5 | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 350 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 110 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | V-0 | UL 94 | |
| 3.2 mm | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weather Resistance - 24 hr (23°C) | 0.10 | % | ASTM D570 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 250 - 300 | °C | |
| Middle Temperature | 250 - 300 | °C | |
| Front Temperature | 250 - 300 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 50 - 60 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM TPS-G 35A | RJM International, Inc. | TPE | RJM |
| SUSTAPEEK MOD | Röchling Sustaplast SE & Co. KG | PEEK | SUSTAPEEK |
| Vi-Chem PVC VDM87-15E/30E-8814 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| INLUBE PBTGF30TF13SI2 | Infinity LTL Engineered Compounds | PBT | INLUBE |
| POTICON RF25X2 | Otsuka Chemical Co., Ltd. | PPS | POTICON |