Plenco 03303 (Injection)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aodgqu_Plenco-03303-Injection-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plenco 03303 is a renumber of Plaslok 5303. Plenco 03303 is a two-stage, mineral and flock-filled phenolic molding compound offering excellent electrical insulating properties. It can be processed by compression, transfer or injection molding . It is UL recognized under file E40654. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.84 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.33 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638 |
| Tensile Strength | 57.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 8630 | MPa | ASTM D790 |
| Flexural Strength | 82.9 | MPa | ASTM D790 |
| Compressive Strength | 180 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18.0 | J/m | ASTM D256 |
| Notched Izod Impact | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 168 | °C | ASTM D648 |
| Continuous Use Temperature | 200 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.1E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 9.2 | kV/mm | ASTM D149 |
| -- 2 | 6.0 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.070 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.35%Heat Resistance, ASTM D794: 200°CDrop Ball Impact, PLENCO Method: 112 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 66.0 - 82.0 | °C | |
| Front Temperature | 82.0 - 99.0 | °C | |
| Processing (Melt) Temp | 104 - 115 | °C | |
| Mold Temperature | 165 - 182 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-8 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titacon® GB925 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Edgetek™ AS-000/000 AS colored UV | PolyOne Corporation | MABS | Edgetek™ |
| Electrafil® J-1305/CF/40 | Techmer Engineered Solutions | PPS | Electrafil® |
| Hostacom X M2 U43 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Jampilen RP340R | Jam Polypropylene Company | PP Random Copolymer | Jampilen |