Infino AE-3060
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | anrbw9_InfinoAE3060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino AE-3060 is a polycarbonate polybutene terephthalate (PC PBT) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.40 - 0.60 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.40 - 0.60 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.40 - 0.60 | % | ISO 2577 |
| Traffic : 3.20mm | 0.40 - 0.60 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2000 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 63.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 61.0 | MPa | ASTM D638 |
| Fracture | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 100 | % | ASTM D638 |
| Fracture | 100 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2300 | MPa | ASTM D790 |
| -- 6 | 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 90.0 | MPa | ASTM D790 |
| -- 8 | 94.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 58 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 150 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 740 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 180 | J/m | ASTM D256 |
| 23°C 10 | 36 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 98.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 86.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 124 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Hot air dryer | 100 | °C | |
| Drying Time | |||
| -- | 4.0 | hr | |
| Hot air dryer | 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 230 - 240 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 40 - 60 | °C | |
| Injection Pressure | 49.0 - 245 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 10 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 10 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titacon® TF920 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Trademark PE LLH2942 | Trademark Plastics Corporation | LLDPE | Trademark PE |
| Amilan® U141 | Toray Resin Company | Nylon 6 | Amilan® |
| Gallonprene® GP210-9002L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LEXAN™ 945 resin | SABIC Innovative Plastics | PC | LEXAN™ |