Lucky Enpla LPB1006F
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | anYIBS_Lucky-Enpla-LPB1006F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lucky Enpla LPB1006F is a polybutene terephthalate (PBT) product,. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Typical application areas are: electrical/electronic applications. The main characteristics are: good weather resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 - 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 51.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2260 | MPa | ASTM D790 |
| Flexural Strength 3 | 71.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 165 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 245 - 265 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Back Pressure | 0.490 - 2.94 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 240-260°CInjection Pressure (1st Pressure): 600-1100 kg/cm²Injection Pressure (2nd Pressure): 400-800 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA B3 HL AZL0309 NT360 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Comai 600-3 BL | Comai Ltda | PP Homopolymer | Comai |
| Esterlloy™ E710T | Asahi Kasei Chemicals Corporation | ABS Alloy | Esterlloy™ |
| Forprene® 6K5901A75VS2 | SO.F.TER. SPA | TPV | Forprene® |
| Hostacom BR 33 G | LyondellBasell Industries | PP, Unspecified | Hostacom |