Desmopan® 5377A
| Category: | TPU-Ester/Ether , Thermoplastic Polyurethane Elastomer (Ester/Ether) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | anL3ky_Desmopan-5377A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; improved microbial resistance; Improved hydrolysis resistance; Application; Cable sheathings; Textile coating; Wristwatch straps; hard to soft systems |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1140 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 77 | ||
| Shore D, 15 sec | 28 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| Break, 23°C | 27.0 | MPa | |
| 10% Strain, 23°C | 1.30 | MPa | |
| 50% Strain, 23°C | 3.60 | MPa | |
| 100% Strain, 23°C | 4.90 | MPa | |
| 300% Strain, 23°C | 8.90 | MPa | |
| Tensile Strain 4(Break, 23°C) | 640 | % | DIN 53504 |
| Abrasion Resistance (23°C) | 80.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 180 | MPa | |
| 20°C | 29.0 | MPa | |
| 60°C | 21.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience | 45 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 5 | 40 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 20 | % | |
| 70°C, 24 hr | 50 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Melt Temperature | 170 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2635D | Teknor Apex Company | TPE | Telcar® |
| Flontech® FT-GR15-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| KW Plastics KWR621 FDA | KW Plastics | PP Copolymer | KW Plastics |
| Karina WHITE PVC COMPOUND BT-0002/17 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sumikon® X655 | SBHPP | Phenolic | Sumikon® |