LNP™ THERMOCOMP™ UF00ASW compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | al5RmM_LNP-THERMOCOMP-UF00ASW-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UF00ASW is a compound based on Polyphthalamide (PPA) containing glass fiber. Characteristics of this grade of Heat Stabilized and Hot Water Moldable. Also known as: LNP* THERMOCOMP* Compound UF-100-10 A HS HW BK8-115 Product reorder name: UF00ASW |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.50 | % | |
| Across Flow : 24 hr | 0.60 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.27 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.33 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19100 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 214 | MPa | |
| Break | 214 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 1.4 | % | |
| Break | 1.5 | % | |
| Flexural Modulus | |||
| 50.0 mm Span 1 | 17500 | MPa | ASTM D790 |
| -- 2 | 17200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 324 | MPa | ISO 178 |
| Yield, 50.0 mm Span 3 | 335 | MPa | ASTM D790 |
| Break, 50.0 mm Span 4 | 337 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 91 | J/m | ASTM D256 |
| 23°C 5 | 9.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 790 | J/m | ASTM D4812 |
| 23°C 6 | 46 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.30 | J | ASTM D3763 |
| -- | 3.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 297 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 7 | 296 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 285 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 8 | 281 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 316 to 321 | °C | |
| Front Temperature | 327 to 332 | °C | |
| Processing (Melt) Temp | 320 to 349 | °C | |
| Mold Temperature | 49.0 to 104 | °C | |
| Back Pressure | 0.170 to 0.500 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LDPE 611A | The Dow Chemical Company | LDPE | DOW™ LDPE |
| BJB Polyurethane TC-891 A/B FR | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Aquivion® P87S-SO2F | Solvay Specialty Polymers | PFSF | Aquivion® |
| Koylene SM250NC | Reliance Industries Limited | PP Homopolymer | Koylene |
| Hostaform® S 27072 WS 10/1570 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |