VALOX™ 830 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | akvoR6_VALOX-830-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Specific Volume | 0.672 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.30 to 0.50 | % | |
| Flow 2 | 0.50 to 0.80 | % | |
| Across Flow 3 | 0.40 to 0.60 | % | |
| Across Flow 4 | 0.60 to 0.90 | % | |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 5 | ASTM D638 | ||
| Yield | 103 | MPa | |
| Break | 107 | MPa | |
| Flexural Modulus 6(50.0 mm Span) | 6890 | MPa | ASTM D790 |
| Flexural Strength 7(Break, 50.0 mm Span) | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 640 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 221 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 193 | °C | |
| CLTE - Flow | ASTM E831 | ||
| -40 to 40°C | 2.5E-5 | cm/cm/°C | |
| 60 to 138°C | 2.5E-5 | cm/cm/°C | |
| RTI Elec | 120 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Oil | 25 | kV/mm | |
| 3.20 mm, in Air | 21 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 | ||
| Arc Resistance 8 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| 2 . | 3.2 to 4.6 mm |
| 3 . | 1.5 to 3.2 mm |
| 4 . | 3.2-4.6 mm |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SE-300P | SHIN-A T&C | Epoxy | SHIN-A |
| NEXT SIGNATURE POMC MF-100 | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT SIGNATURE |
| Durethan® BG 30 X FN01 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| LARIPUR® LPR 5260 | COIM S.p.A. | TPU-Polyether | LARIPUR® |
| INELEC PEICF30 | Infinity LTL Engineered Compounds | PEI | INELEC |