TAROMID B 280 MT5
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | akU5Fe_TAROMID-B-280-MT5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 medium viscosity 25% mineral filled, good dimensional stability, uniform shrinkage in all directions, good surface appearance, mechanical and thermal properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 - 1.34 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.40 - 0.60 | % | Internal method |
| Flow direction | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.0 | % | ISO 62 |
| Saturated, 23°C | 6.8 | % | ISO 62 |
| Granule Humidity 1 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(750°C) | 25 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 78.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 6200 | MPa | ISO 178 |
| Flexural Stress 4 | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Notched Izod Impact (23°C) | 4.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed) | 180 | °C | ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 6 | 70.0 | °C | IEC 60216 |
| -- 7 | 100 | °C | IEC 60216 |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Ball Pressure Test (170°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 222 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 24 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | 20,000 hr, 110 H |
| 7 . | Short term, 150 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GA-3680 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| STARFLEX® D2285 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | STARFLEX® |
| Andur 7501 DPLF/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| K-Prene SHEATHING EPR 5064 | Technovinyl Polymers India Ltd. | MPR | K-Prene |
| PENTAMID B GK30 H LS black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |