KIBISAN® PN-107
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | KIBISAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | akCoui_KIBISANPN107.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KIBISAN®PN-107 is a styrene propylene fine (SAN) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.06 | g/cm³ | ASTM D792 |
| 23°C | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 58.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.20 - 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 83 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 2 | 60.7 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Fracture | 65.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 3 | 5.0 | % | ASTM D638 |
| Fracture | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 4 | 3450 | MPa | ASTM D790 |
| -- 5 | 2600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 6 | 88.3 | MPa | ASTM D790 |
| -- 7 | 89.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 18 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 17 | J/m | ASTM D256 |
| 23°C | 2.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, not annealed | 88.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 99.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ASTM D1525, ISO 306/A50 7 8 |
| -- | 101 | °C | ISO 306/B50 |
| CLTE - Flow | 3.6E-5 - 3.8E-5 | cm/cm/°C | ISO 11359-2 |
| Heat Deflection Temperature | ASTM D648 | ||
| Annealed | 100 | °C | ASTM D648 |
| Unannealed | 90 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75 - 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 160 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 180 - 210 | °C | |
| Mold Temperature | 40 - 60 | °C | |
| Injection Pressure | 4.90 - 6.86 | MPa | |
| Holding Pressure | 3.92 - 5.88 | MPa | |
| Back Pressure | 0.490 - 1.47 | MPa |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 6.0 mm/min |
| 3 . | 6.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-SP90 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Xuchuan XCM-310S | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Flontech® FT-COND2-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Dynaglide® DW 612 | DeWAL Industries | PTFE | Dynaglide® |
| LNP™ THERMOCOMP™ DX07350 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |