INSULCAST® 136/INSULCURE 9
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aiz95L_INSULCAST-136-INSULCURE-9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 136 is an easy to use epoxy casting/potting compound exhibiting excellent adhesion to metals, ceramics and most plastics. When properly cured with INSULCURE 11B, INSULCAST 136 will conform to the requirements of MIL-I-16923, Types B, C & D, and will not support fungus growth. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 to 4.0 | % | ASTM D638 |
| Flexural Strength | 107 | MPa | ASTM D790 |
| Compressive Strength | 103 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 4.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.72 | W/m/K | |
| Heat Deflection Temperature | 80 | °C | |
| Service Temperature | 105 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear Shrinkage | 0.20 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.80 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 6.0 to 7.0 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Shelf Life | 52 | wk | |
| Post Cure Time (150°C) | 1.0 | hr |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Amber | ||
| -- 2 | Black | ||
| Density | |||
| -- 3 | 0.968 | g/cm³ | |
| -- 4 | 1.59 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| -- 5 | 0.055 | Pa·s | |
| -- 6 | 30 | Pa·s | |
| -- 7 | 80 | Pa·s | |
| Curing Time | |||
| 65°C | 1.0 | hr | |
| 25°C | 16 to 24 | hr | |
| Pot Life (25°C) | 30 | min |
| Note Message | |
|---|---|
| 1 . | INSULCURE 9 |
| 2 . | INSULCAST 136 |
| 3 . | INSULCURE 9 |
| 4 . | INSULCAST 136 |
| 5 . | INSULCURE 9 |
| 6 . | Mixed |
| 7 . | INSULCAST 136 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8744 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Sindustris ABS LRS911D | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Synprene™ RT-5155 RoHS Natural | PolyOne Corporation | SBC | Synprene™ |
| Flexathene® TP38NC01X01 | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| LUVOCOM® 1301-8582 | LEHVOSS Group | PPS | LUVOCOM® |