Kepital® TE-24S
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ailtYS_Kepital-TE-24S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A high viscosity grade for general injection molding. It was modified with elastomer, and so suitable for parts requiring super impact resistance and excellent toughness. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 2.5 | g/10 min | ASTM D1238 |
| -- | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 2.00mm | 1.3 | % | ASTM D955 |
| 3.00 mm | 1.5 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.25 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 35.0 | MPa | ASTM D638 |
| Yield, 23°C | 38.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | < 300 | % | ASTM D638 |
| Nominal Tensile Strain at Break | > 100 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1250 | MPa | ASTM D790 |
| 23°C | 1300 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 41.0 | MPa | ASTM D790 |
| 23°C | 46.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 28 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 77.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 61.0 | °C | ISO 75-2/A |
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| CLTE - Flow (20 to 80°C) | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+16 | ohms | ASTM D257 |
| -- | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Additional Information |
|---|
| Tensile Elongation @ Brk, ASTM D638, 23°C: < 300% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3506 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| REVOLVE® M-505 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| Vinnolit® S 4170 | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Electrafil® PA6/6 G/CF15 C - 3 BK | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| Kepital® LX-30 BK | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |