NANCAR® 1042
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | Nantex Industry Co., Ltd. |
| Trademark: | NANCAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ai8B7x_NANCAR-1042.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NANCAR® 1042 is a medium high acrylonitrile butadiene copolymer with good oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It has high Mooney viscosity and provides compounds with higher strength and modulus. NANCAR® 1042 is a general purpose and easy processing nitrile elastomer. It has excellent solubility, milled and unmilled. It is recommended for use in seals, hoses, belts, sheetings, print rolls, gaskets, kitchen mats, shoe soles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | |
| Mooney Viscosity (ML 1+4, 100°C) | 79 | MU | ASTM D1646 |
| Acrylonitrile Content - Bound | 33.0 | % | Internal Method |
| Solubility - in MEK | 100 | % | |
| Stabilizer | Slightly-staining |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | 0.40 | % | ASTM D5688 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A 1 | 72 | ||
| Shore A 2 | 71 | ||
| Shore A 3 | 70 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 300% Strain 4 | 12.4 | MPa | |
| 300% Strain 5 | 13.3 | MPa | |
| 300% Strain 6 | 14.5 | MPa | |
| Tensile Strength | ASTM D412 | ||
| Yield 7 | 26.3 | MPa | |
| Yield 8 | 26.9 | MPa | |
| Yield 9 | 25.8 | MPa | |
| Tensile Elongation | ASTM D412 | ||
| Break 10 | 530 | % | |
| Break 11 | 510 | % | |
| Break 12 | 490 | % | |
| Tear Strength | 58.8 | kN/m | ASTM D624 |
| Compression Set 13(100°C, 70 hr) | 58 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 14(100°C, 70 hr) | -4.0 | % | ASTM D865 |
| Change in Ultimate Elongation in Air 15(100°C, 70 hr) | -22 | % | ASTM D865 |
| Change in Durometer Hardness in Air 16(Shore A, 100°C, 70 hr) | 3.0 | ASTM D865 | |
| Change in Tensile Strength 17 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -1.0 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -10 | % | |
| Change in Ultimate Elongation 18 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -14 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -14 | % | |
| Change in Durometer Hardness 19 | ASTM D471 | ||
| Shore A, 100°C, 70 hr, in ASTM #1 Oil | -2.0 | ||
| Shore A, 100°C, 70 hr, in ASTM #3 Oil | -13 | ||
| Change in Volume 20 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM Oil #1 | 0.0 | % | |
| 100°C, 70 hr, in ASTM Oil #3 | 18 | % |
| Note Message | |
|---|---|
| 1 . | Cured for 60.0 min at 150°C |
| 2 . | Cured for 40.0 min at 150°C |
| 3 . | Cured for 20.0 min at 150°C |
| 4 . | Cured for 20.0 min at 150°C |
| 5 . | Cured for 40.0 min at 150°C |
| 6 . | Cured for 60.0 min at 150°C |
| 7 . | Cured for 60.0 min at 150°C |
| 8 . | Cured for 40.0 min at 150°C |
| 9 . | Cured for 20.0 min at 150°C |
| 10 . | Cured for 20.0 min at 150°C |
| 11 . | Cured for 40.0 min at 150°C |
| 12 . | Cured for 60.0 min at 150°C |
| 13 . | Cured for 60.0 min at 150°C |
| 14 . | Cured for 40.0 min at 150°C |
| 15 . | Cured for 40.0 min at 150°C |
| 16 . | Cured for 40.0 min at 150°C |
| 17 . | Cured for 40.0 min at 150°C |
| 18 . | Cured for 40.0 min at 150°C |
| 19 . | Cured for 40.0 min at 150°C |
| 20 . | Cured for 40.0 min at 150°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R210A85UV | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyether | Ravathane |
| Ad-Tech Polyester NO. 31M BOAT BONDING | Ad-Tech Plastic Systems Corp. | Polyester, TS | Ad-Tech Polyester |
| FRAGOM PR/555 K1 | Crosspolimeri S.p.A. | EVA | FRAGOM |
| Kepamid® 1500SF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| LNP™ THERMOCOMP™ RF004S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |