BESTNYL SI20CI01AHQ03
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ah5Rws_BESTNYL-SI20CI01AHQ03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Poliamida 6 natural 20% glass fibre with heat stabilized and 5%nano charges wich create a barrier against external atmospherical agents and also improves dimensional and enlighten the final application furthermore produces better final surface. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.29 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 7.0 | -- | g/10 min | ISO 1133 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5200 | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 113 | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 3.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 | 45 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 180 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 235 | -- | °C | ISO 306 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+12 | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Humidity Pellets, ISO 1110: 0.2%Flammability Speed, FMV 302:<100 mm/minAshes, Triesa Test: 25% |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 230 - 240 | °C | |
| Mold Temperature | 70.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VR VRGR 907 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| TPC PVC SM76E | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Westlake LDPE EF923 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| XIRAN® IZ1018M | Polyscope Polymers BV | SMA | XIRAN® |
| XANTAR® LDS 3732 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® LDS |