LNP™ STAT-KON™ DX05474 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | agmgQL_LNPSTATKONDX05474compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DX05474 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Retardant, Mold Release. Also known as: LNP* STAT-KON* Compound DC-1002 EM FR MR Product reorder name: DX05474 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.51 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.36 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13800 | MPa | ASTM D638 |
| -- | 7680 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 105 | MPa | ASTM D638 |
| Fracture | 107 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 5.9 | % | ASTM D638 |
| Fracture | 6.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7580 | MPa | ASTM D790 |
| -- | 7300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 159 | MPa | ASTM D790 |
| -- | 169 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 8.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 370 | J/m | ASTM D4812 |
| 23°C 3 | 28 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 296 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 150 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 291 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 146 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 4.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.0E+7 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® 1021GF6 BRIGHT | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| Ferro PP LPP20BC06WH | Ferro Corporation | PP, Unspecified | Ferro PP |
| Durethan® BKV 40 H2.0 901510 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |
| GPPC PS-316 | GPPC Chemical Co., Ltd. | PS (HIPS) | GPPC |
| POLYform C M20 | Polykemi AB | Acetal (POM) Copolymer | POLYform C |