Razamid® B111
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Razin™ Engineering Plastics |
| Trademark: | Razamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | agRcGw_Razamid-B111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Razamid B111 is a general purpose injection grade natural color polyamide 6 resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 85.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 2600 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 3.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 190 | °C | |
| 1.8 MPa, Unannealed | 70.0 | °C | |
| Vicat Softening Temperature | 200 | °C | ASTM D1525 |
| Peak Melting Temperature | 210 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 220 to 245 | °C | |
| Middle Temperature | 225 to 260 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 25.0 to 95.0 | °C | |
| Injection Pressure | 35.0 to 140 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 8010 | Formosa Plastics Corporation | HDPE | TAISOX |
| Sylvin 8716-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vinnolit® SA 1062/7 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| ExxonMobil™ LDPE LD 100BW Wire & Cable | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| LNP™ STAT-KON™ DX03633C compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |