Ateva® 1081
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | agMhih_Ateva-1081.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for film extrusions requiring superior sealability and strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.933 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 9.0 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - 1% Secant | 123 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D882A | ||
| MD : Break | 23.0 | MPa | |
| TD : Break | 24.0 | MPa | |
| Tensile Elongation 2 | ASTM D882A | ||
| MD : Break | 380 | % | |
| TD : Break | 550 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 82.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 102 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide PF003U | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Nymax™ GF 1200 A 55 HS Black 13 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Gallonprene® GP210-6006 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| POLYfill PPH K20020 | Polykemi AB | PP Homopolymer | POLYfill |
| NORYL™ NH6010B resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |