Hostaform® MT® SlideX™ 1203
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | agEthu_Hostaform-MT-SlideX-1203.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostaform® acetal copolymer grade MT® SlideX™ 1203 is a special grade developed for medical industry applications containing low residual monomers and no animal products. Hostaform® MT® SlideX™1203 is a standard flow injection molding grade with tribological modification designed for use in demanding applications that require prevention of audible noise caused by stick-slip phenomenon and low friction and wear against plastics and metals. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.7 | % | ISO 294-4 |
| Flow direction | 2.0 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2650 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 58.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 12 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 45 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 150 | kJ/m² | ISO 179/1eU |
| 23°C | 160 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 93.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 170 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Nozzle Temperature | 190 - 210 | °C | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 4.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 60 to 80°CZone 4 Temperature: 190 to 210°CManifold Temperature: 190 to 210°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene CD-471 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| TOTAL Polypropylene PPC 4720WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| VALOX™ 7062HP resin | SABIC Innovative Plastics Asia Pacific | PBT | VALOX™ |
| Hifax EKC 287P | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Monprene® RG-17260 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |