SEETEC LLDPE UF317
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | SEETEC LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aeyFT2_SEETEC-LLDPE-UF317.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UF317 is manufactured by Unipol process technology. UF317 has good mechanical properties, excellent optical properties and good processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 42.2 | MPa | |
| TD : Break, 40 µm, Blown Film | 38.2 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 740 | % | |
| TD : Break, 40 µm, Blown Film | 760 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 170 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 40.0 µm | 58.8 | kN/m | |
| TD : 40.0 µm | 107.9 | kN/m |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 70 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 16 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® M TM6MED (Series: MC/tl) | KRAIBURG TPE | TPE | THERMOLAST® M |
| VECTRA® MT4310 | Celanese Corporation | LCP | VECTRA® |
| ADENE NCQAG | A.D. Compound spa | PP Copolymer | ADENE |
| IDI BMC Rosite 3550D | IDI Composites International | TS, Unspecified | IDI BMC |
| TARFLON™ #1700 | Formosa Idemitsu Petrochemical Corporation | PC | TARFLON™ |