UMG ALLOY® TC-80A
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | UMG ABS, Ltd. |
| Trademark: | UMG ALLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aeQCuf_UMG-ALLOY-TC-80A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UMG ALLOY® TC-80A is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific or North America for injection molding. Primary attribute of UMG ALLOY® TC-80A: RoHS Compliant. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.50 to 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 107 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1900 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 48.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 79.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 107 | °C | ISO 75-2/Af |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 270 | °C | |
| Nozzle Temperature | 220 to 250 | °C | |
| Processing (Melt) Temp | 230 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 70.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 5.00 to 15.0 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP7120F B1 | Spartech Polycom | PP, Unspecified | Spartech |
| Haysite BMC 14100 | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| Jam PE 32604 | Jam Petrochemical Company | LLDPE | Jam PE |
| Karina GREEN PVC COMPOUND 813D40/ 88-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OnFlex™ U 5355A-S0014 | PolyOne Corporation | TPE | OnFlex™ |