Quadrant EPP PC 1000
| Category: | PC , Polycarbonate |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | adfLgG_Quadrant-EPP-PC-1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Quadrant EPP PC 1000 is a Polycarbonate (PC) product. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.00 mm | 0.18 | % | |
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 3.00 mm 1 | 13.0 | mg | |
| 23°C, 3.00 mm 2 | 0.33 | % | |
| 23°C, 3.00 mm 3 | 23.0 | mg |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Service Temperature - Minimum | -60 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 10.0 mm) | 75 | ISO 2039-2 | |
| Ball Indentation Hardness (10.0 mm) | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 4 | 2400 | MPa | ISO 527-2/1B/1 |
| Tensile Stress 5(Yield) | 70.0 | MPa | ISO 527-2/1B/20 |
| Tensile Strain 6(Break) | > 50 | % | ISO 527-2/1B/20 |
| Tensile Creep Modulus (1000 hr) | 17.0 | MPa | ISO 899-1 |
| Compressive Stress | ISO 604/1 | ||
| 5% Strain | 72.0 | MPa | |
| 2% Strain | 35.0 | MPa | |
| 1% Strain | 18.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength 7 | 9.0 | kJ/m² | ISO 180/2A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 130 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 8 | 115 | °C | |
| -- 9 | 125 | °C | |
| -- 10 | 135 | °C | |
| Glass Transition Temperature | 150 | °C | |
| CLTE - Flow | |||
| 23 to 100°C | 6.5E-5 | cm/cm/°C | |
| 23 to 150°C | 6.5E-5 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.21 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11 | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity 12 | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength 13(1.00 mm, in Oil) | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz 14 | 3.00 | ||
| 1 MHz 15 | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz 16 | 1.0E-3 | ||
| 1 MHz 17 | 8.0E-3 | ||
| Comparative Tracking Index 18 | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | ||
| 6.00 mm | HB | ||
| Oxygen Index | 25 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Weight, 24 hrs |
| 2 . | 96 hrs |
| 3 . | Weight, 96 hrs |
| 4 . | Conditioned |
| 5 . | Conditioned |
| 6 . | Conditioned |
| 7 . | Conditioned |
| 8 . | 20000 hrs |
| 9 . | 5000 hrs |
| 10 . | Short periods |
| 11 . | Conditioned |
| 12 . | Conditioned |
| 13 . | Conditioned |
| 14 . | Conditioned |
| 15 . | Dry |
| 16 . | Dry |
| 17 . | Conditioned |
| 18 . | Conditioned |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP PSU 1000 | Quadrant Engineering Plastic Products | PSU | Quadrant EPP |
| ExxonMobil™ PP3295G1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Hifax DRS715X | LyondellBasell Industries | TPO (POE) | Hifax |
| EvoSource™ PC/ABS 5366 90/04 | MBA Polymers Austria Kunststoffverarbeitung GmbH | PC+ABS | EvoSource™ |
| LNP™ VERTON™ RV008ES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |