Hostalen PP H2483
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | adZFo2_Hostalen-PP-H2483.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen PP H2483 is a natural polypropylene copolymer with an exceptional mechanical properties balance. The product has been specifically designed for extrusion of pipes for underground drainage and sewage applications but can also be used for injection moulding and other extrusion applications. The product provides very high stiffness, excellent impact resistance at room temperature and in particular at sub-zero temperatures with high heat- and extraction stability. The material Hostalen PP H2483 has not been tested and therefore has not been certified for pressure applications. For further details about the suitable applications for this material please contact LyondellBasell. Hostalen PP H2483 is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/5.0 kg | 0.50 | g/10 min | |
| 230°C/2.16 kg | 0.30 | g/10 min | |
| 230°C/5.0 kg | 1.3 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant 1(23°C) | 1800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 32.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 8.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.3 | kJ/m² | |
| 0°C | 11 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 159 | °C | ISO 306/A50 |
| Oxidation Induction Time (210°C) | 25 | min | ISO 11357-6 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | After 7 days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® A1600 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| AIE PPO 9010F-S120E | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
| Capran® UNIDRAW 102 | Honeywell | Nylon 6 | Capran® |
| Kepital® F20-03H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Pibiter® HI A1301 NAT001 | SO.F.TER. SPA | PBT | Pibiter® HI |