Oleflex™ 6261-70A-8843 Black, 307105
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Oleflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | adR2eh_Oleflex-6261-70A-8843-Black-307105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Oleflex™6261-70A-8843 Black, 307105 is a thermoplastic elastomer (TPE) material,. This product is available in North America,. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shao A, mm) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5A | ||
| 2.00 mm | 2.60 | MPa | ISO 527-2/5A |
| 70°C, 2.00 mm 1 | 2.60 | MPa | ISO 527-2/5A |
| Tensile Strain | ISO 527-2/5A | ||
| Fracture, 2.00mm | 500 | % | ISO 527-2/5A |
| Fracture, 70°C, 2.00mm 2 | 470 | % | ISO 527-2/5A |
| Wear resistance (mm) 3 | 5000 | SAE J948 |
| Thermal | Nominal Value | ||
|---|---|---|---|
| Cold flexibility- High and Low Bend Test | |||
| -30°C, 2.54 cm | Pass | ||
| -24°C, 2.54 cm | Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Combustibility (mm) | 33 | mm/min | FMVSS 302 |
| Atomization (mm) 4 | 99.0 | SAE J1756 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Surface Temperature - Heat Resistance (85°C, 2.00 mm) 5 | 5.00 | ||
| Xenon Arc - Delta E 6 | 0.0700 | SAE J1885 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (2.00 mm) | 17.8 | kN/m | ASTM D624 |
| Compression Set | |||
| 70°C, 7 hr | 47 | % | ASTM D395 |
| 70°C, 22 hr | 49 | % | ASTM D395B |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Hot Odor Test, SAE J1351: 1.4 |
| Note Message | |
|---|---|
| 1 . | After 7 h @ 70°C |
| 2 . | After 7 h @ 70°C |
| 3 . | Tested according to SAE J948/ASTM D3884 |
| 4 . | Method B |
| 5 . | 168 h @ 85°C |
| 6 . | 200 hours, 267 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4PET® 9L22120 HIUV | 4Plas | PET | 4PET® |
| Epiall® 1908-1 | Sumitomo Bakelite North America, Inc. | Epoxy | Epiall® |
| Karina BLACK PVC COMPOUND 814-48/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Panlite® L-1225Z100 | TEIJIN LIMITED | PC | Panlite® |
| POLYCOMPO PE 3000B | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |