Tarnamid® T- 27 GF30 TF15
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | adDPYr_Tarnamid-T--27-GF30-TF15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tarnamid T-27 GF30TF15 is tribological modified grade, which cause decrease coefficient of friction and wear. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 15.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 2.00 mm | 1.1 | -- | % | |
| Flow : 2.00 mm | 0.10 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 160 | 130 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 8300 | MPa | ISO 527-2/5 |
| Tensile Stress (Yield) | 160 | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 6.0 | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 9000 | 6500 | MPa | ISO 178 |
| Flexural Stress 2 | 240 | 185 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (-30°C) | 15 | 18 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 200 | 140 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | 190 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | 205 | °C | ISO 306/B |
| Melting Temperature | 221 | -- | °C | ISO 11357-3 |
| Limit of Temperature - a few hours operation | < 180 | -- | °C | |
| Temperature Index | ||||
| 20000 hr | 110 | -- | °C | |
| 5000 hr | 120 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA6, MHR, 14-080, GF30Z15 | -- | ISO 1874 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.20 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 50 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TERRAMAC TP-4000 | UNITIKA Plastics Division | PLA | TERRAMAC |
| Sylvin 8260-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| StarMed® 9040-0007 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMed® |
| Monprene® MP-1500 | Teknor Apex Company | TPE | Monprene® |
| Silastic® Q7-4750 | Dow Corning Corporation | Silicone | Silastic® |