AGILITY™ 1001 Performance LDPE
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AGILITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | abv8GG_AGILITY-1001-Performance-LDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AGILITY™ 1001 Performance LDPE is a high pressure LDPE resin designed specifically to run at faster output rates on blown film lines in blends with LLDPE resins while maintaining bubble stability. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.65 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 1.02 | J | |
| Film Puncture Force | 31.1 | N | |
| Film Puncture Resistance | 4.96 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 26.5 | J/cm³ | ASTM D882 |
| TD | 53.8 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 236 | MPa | ASTM D882 |
| 2% secant, MD | 216 | MPa | ASTM D882 |
| 1% secant, TD | 297 | MPa | ASTM D882 |
| 2% secant, TD | 256 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 27.6 | MPa | ASTM D882 |
| TD : Yield | 12.8 | MPa | ASTM D882 |
| MD : Fracture | 28.6 | MPa | ASTM D882 |
| TD : Fracture | 16.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 120 | % | ASTM D882 |
| TD : Fracture | 440 | % | ASTM D882 |
| Dart Drop Impact | 70 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 270 | g | ASTM D1922 |
| TD | 95 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 109 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 54 | ASTM D2457 | |
| Haze | 9.0 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 3.5 in. Screw Type: DSB II Die Gap: 70 mil Melt Temperature: 398°F Output: 12 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 56 rpm Frost Line Height: 37 in. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime ABS Weather-X ML500 | Primex Plastics Corporation | ABS | Prime ABS Weather-X |
| GATONE™ 5600 | Solvay Specialities India Private Limited (SSIPL) | PEEK | GATONE™ |
| Lucent PC PC/PBT-1830 | Lucent Polymers, Inc. | PC+PBT | Lucent PC |
| TECHNYL® A 218 Y10 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Sylvin 4215-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |