PROTEQ™ C35UST2
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | abeEF5_PROTEQ-C35UST2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ C35UST2 is one of the higher melt flow automotive polypropylene copolymers which contains 10% talc filler and features improved heat ageing and UV performance. PROTEQ™ C35UST2 has been designed to meet the stringent requirements of automotive exterior and interior trim durability specifications, combining easy processing with rigidity, toughness and heat resistance. Typical automotive interior applications are consoles, seat bolsters, steering shrouds, door liners and glovebox lids. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 34 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 71 | ||
| Shore D, 15 sec | 63 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2050 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 55 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 118 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 65.0 | °C | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 195 to 215 | °C | |
| Middle Temperature | 205 to 225 | °C | |
| Front Temperature | 215 to 235 | °C | |
| Processing (Melt) Temp | 220 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PH 82 T 20 | SILON s.ro | PP Homopolymer | TABOREN |
| ColorFast® PBT100 | LTL Color Compounders, Inc. | PBT | ColorFast® |
| Ferro PP TPP35AC23NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| HiFill® PA6 GF/M25 HS L BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| HIVOREX 5000S | Lotte Chemical Corporation | HDPE | HIVOREX |