ZEONOR® 1060R
| Category: | COP , Cyclo Olefin Polymer |
| Manufacturer: | Zeon Corporation |
| Trademark: | ZEONOR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | abGB1R_ZEONOR-1060R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ZEONOR® is a new line of thermoplastic polyolefin resin with an excellent combination of optical and electronic properties. These unique Cyclo Olefin Polymer (COP) was developed by ZEON CORPORATION using proprietary technology for a wide range of electronic, automotive and packaging applications. ZEONOR can easily be processed for any of these applications by injection molding, blow molding or extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 14 | g/10 min | |
| 280°C/2.16 kg | 60 | g/10 min | |
| Water Absorption (Equilibrium) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 20 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Tensile Stress | 53.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 60 | % | ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 18 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 99.0 | °C | ASTM D648 |
| Glass Transition Temperature | 100 | °C | JIS K7121 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 70 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.30 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 2.0E-4 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3000 µm) | 92.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| DuPont Impact Strength | 26.0 | J |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3568 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| VENELENE® FD-0348 | Poliolefinas Internacionales, C.A. (Polinter) | LDPE | VENELENE® |
| AIE PPO 9010F-S085A | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
| Europrene® SOL B 183 | Versalis S.p.A. | SBR, Solution | Europrene® |
| LEXAN™ 241R resin | SABIC Innovative Plastics | PC | LEXAN™ |