Order Products : sales@su-jiao.com
Xuchuan A-9008/B-6118
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Xuchuan Chemical (Suzhou) Co., Ltd |
| Trademark: | Xuchuan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ab2Nv0_Xuchuan-A-9008-B-6118.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Xuchuan A-9008/B-6118 is a Thermoplastic Polyurethane Elastomer (Polyester) (TPU-Polyester) product. It is available in Asia Pacific. Typical application: Consumer Goods. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.300 to 0.400 | g/cm³ | |
| Density | |||
| A-9008 : 40°C | 1.010 to 1.020 | g/cm³ | |
| B-6118 : 40°C | 1.080 to 1.200 | g/cm³ | |
| Viscosity | |||
| A-9008 : 40°C | 1.00 to 1.30 | Pa·s | |
| B-6118 : 40°C | 0.600 to 0.800 | Pa·s |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| DIN Abrasion | 130 to 200 | mm³ |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time | 6.0 to 8.0 | sec | |
| End of Rise Time | 30.0 to 40.0 | sec |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Free Rise Foam Density | 210 to 260 | kg/m³ | |
| Preheat Temperature | |||
| Part A | 50 to 60 | °C | |
| Part B | 50 to 60 | °C | |
| Preheat Time | |||
| Part A | 6.0 to 8.0 | hr | |
| Part B | 6.0 to 8.0 | hr | |
| Processing Temperature | |||
| Part A | 40 to 45 | °C | |
| Part B | 38 to 42 | °C |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 60 to 88 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 4.00 to 7.00 | MPa | |
| Tensile Elongation (Break) | 200 to 300 | % | |
| Tear Strength | 11.0 to 20.0 | kN/m |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 110 | ||
| Demold Time | 5.0 to 7.0 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 45.0 to 55.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 3206 | Covestro - Polycarbonates | PC | Makrolon® |
| TAROMID B 240 MT2 Y2 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Vydyne® 47H | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Fainplast PVC RL 708 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Plaslube® J-4/30/TF/13/SI/2 NAT | Techmer Engineered Solutions | Nylon 612 | Plaslube® |