LNP™ THERMOCOMP™ JF004E compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aaa0nA_LNPTHERMOCOMPJF004Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound JF-1004 EM Product reorder name: JF004E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.25 - 0.45 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 128 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 6000 | MPa | ISO 178 |
| Flexural Stress | 178 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 223 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 218 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1750 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Akulon® K222-DL | DSM Engineering Plastics | Nylon 6 | Akulon® |
| APEX® 1003 | Teknor Apex Company | PVC, Flexible | APEX® |
| 3M™ Dyneon™ PTFE Compound TF 8465 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| LNP™ THERMOCOMP™ JF004 compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |