The Honeywell Halar® E-Series ECTFE film is a high performance film with excellent mechanical, electrical and release properties. It is non-flammable, and has outstanding chemical resistance. Halar E-Series Film is available in the following colors: Blue, White and Clear.

General Information
Features	Good electrical performance Good chemical resistance Good demoulding performance
Uses	Films
Appearance	White Blue Clear/transparent
Forms	Films

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.68	g/cm³	ASTM D792

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With Metal-Dynamic	0.28	ASTM D1894
With self-dynamics	0.58	ASTM D1894

Films	Nominal Value	Unit	Test Method
secant modulus			ASTM D882
MD	1930	MPa	ASTM D882
TD	1520	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield	35.2	MPa	ASTM D882
TD : Yield	31.0	MPa	ASTM D882
MD : Fracture	83.8	MPa	ASTM D882
TD : Fracture	57.6	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	180	%	ASTM D882
TD : Fracture	280	%	ASTM D882
Water Vapor Transmission Rate (38°C, 100% RH)	0.20	g·mm/m²/atm/24 hr	ASTM F1249

Thermal	Nominal Value	Unit	Test Method
Peak Crystallization Temperature (DSC)	240	°C	ASTM D3418

Additional Information
Yield: 16490 in²/lbTensile Strength @ Yield, ASTM D 882, MD: 4500 to 5700 psiTensile Strength @ Yield, ASTM D 882, TD: 4000 to 5000 psiTensile Strength @ Break, ASTM D 882, MD: 88000 to 15500 psiTensile Strength @ Break, ASTM D 882, TD: 6200 to 10500 psiElongation @ Break, ASTM 882, MD: 90 to 275%Elongation @ Break, ASTM 882, TD: 210 to 355%Secant Modulus, ASTM D 882, MD: 230000 to 330000 psiSecant Modulus, ASTM D 882, TD: 190000 to 250000 psiGraves Tear (initial), ASTM D 1004, MD: 400 to 570 g/milGraves Tear (initial), ASTM D 1004, TD: 350 to 2700 g/milDimensional Stability, ASTM D1204, 300°F, 10 min: <3% shrinkageCoef of Friction, ASTM D1894, Vs Metal - Dynamic: 0.23 to 0.33Coef of Friction, ASTM D1894, Vs Itself - Dynamic: 0.30 to 0.86

Additional Information

Yield: 16490 in²/lbTensile Strength @ Yield, ASTM D 882, MD: 4500 to 5700 psiTensile Strength @ Yield, ASTM D 882, TD: 4000 to 5000 psiTensile Strength @ Break, ASTM D 882, MD: 88000 to 15500 psiTensile Strength @ Break, ASTM D 882, TD: 6200 to 10500 psiElongation @ Break, ASTM 882, MD: 90 to 275%Elongation @ Break, ASTM 882, TD: 210 to 355%Secant Modulus, ASTM D 882, MD: 230000 to 330000 psiSecant Modulus, ASTM D 882, TD: 190000 to 250000 psiGraves Tear (initial), ASTM D 1004, MD: 400 to 570 g/milGraves Tear (initial), ASTM D 1004, TD: 350 to 2700 g/milDimensional Stability, ASTM D1204, 300°F, 10 min: <3% shrinkageCoef of Friction, ASTM D1894, Vs Metal - Dynamic: 0.23 to 0.33Coef of Friction, ASTM D1894, Vs Itself - Dynamic: 0.30 to 0.86

Category:	PCTFE , Polychlorotrifluoroethylene
Manufacturer:	Honeywell
Trademark:	Honeywell Halar
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	aZ9GHm_Honeywell-Halar-E1000.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 199 X 132495 A	RTP Company	PP, Unspecified	RTP
RTP 201H UV HS	RTP Company	Nylon 66	RTP
MBA PP 2126	MBA Polymers	PP Impact Copolymer	MBA PP
Axiall PVC 39041	Axiall Corporation	PVC, Flexible	Axiall PVC
PHOENIX™ 6301	Phon Tech Industrial Company	TPE	PHOENIX™