Self-lubricating product based on Polycarbonate (PC). PTFE. Product UL certified. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 0.75 | % | |
| Flow : 2.00 mm | 0.55 to 0.75 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 110 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 8.0 | % | |
| Coefficient of Friction | ASTM D3702 | ||
| vs. Itself - Dynamic | 0.14 | ||
| vs. Itself - Static | 0.18 | ||
| Wear Factor | 3.50E-10 | (m³/h)/(N·m·h) | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 130 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | V-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 265 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPR-30G Nat | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| BJB Polyurethane F-85 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Huafon HF-1265AP | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Sylvin 5175-92 White 1542 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| UNITIKA Nylon 6 RUN35-TA | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |