Latamid 12 H FE90
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aYkly9_Latamid-12-H-FE90.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 12 (PA 12). Heat stabilised. Magnetizable filler. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 3.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.70 to 0.90 | % | |
| Flow : 2.00 mm | 0.70 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 35.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 110 | °C | |
| Vicat Softening Temperature | 160 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2501TH00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Zhongfa PC/ABS CH-110 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC+ABS | Zhongfa |
| Dynaglide® DW 602 | DeWAL Industries | PTFE | Dynaglide® |
| INEOS PP H53N-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| LNP™ VERTON™ RVL36 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ VERTON™ |