MARPOL® LL6F 803
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aYP5Oe_MARPOL-LL6F-803.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: MARPOL® LL6F 803 is a hexene LLDPE cast film resin with excellent tensile, stiffness and toughness properties. This resin also displays superior drawability and is versatile in packaging applications. Recommended Applications Packaging films, cast film and cast stretch film |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 117 | MPa | |
| 1% Secant, TD | 124 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 6.89 | MPa | |
| TD : Yield | 6.76 | MPa | |
| MD : Break | 58.6 | MPa | |
| TD : Break | 36.5 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 560 | % | |
| TD : Break | 830 | % | |
| Dart Drop Impact | 90 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 250 | g | |
| TD | 570 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 91 | ASTM D2457 | |
| Haze | 1.7 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP5930R B1 | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| TOTAL Polyethylene EVA 1005 VN 35 | TOTAL Refining & Chemicals | EVA | TOTAL Polyethylene |
| APEX® 3070 | Teknor Apex Company | PVC, Flexible | APEX® |
| Kepital® F25-03H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| LNP™ THERMOCOMP™ PF00ASXS compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |