Halar® 700 HC
| Category: | ECTFE , Ethylene Chlorotrifluoroethylene Copolymer |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Halar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aXgpT0_Halar-700-HC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Halar® 700 HC is an Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion. Important attributes of Halar® 700 HC are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 7.0 to 10 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | < 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 1320 | MPa | ASTM D882 |
| Tensile Strength 2 | ISO 527-3 | ||
| Yield, 23°C | 28.5 | MPa | |
| Break, 23°C | 41.4 | MPa | |
| Tensile Elongation 3 | ISO 527-3 | ||
| Yield, 23°C | 5.0 | % | |
| Break, 23°C | 310 | % | |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.20 | ASTM D1894 | |
| Taber Abrasion Resistance (1000 Cycles, 500 g, CS-17 Wheel) | 16.5 | mg | ASTM D4060 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Trouser Tear (23°C, 3.20 mm) | 420.0 | kN/m | DIN 53363 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crystallization Heat | 22.7 | J/g | ASTM D3418 |
| Heat of Fusion | 24.0 | J/g | ASTM D3418 |
| Thermal Stability - 1% mass loss, N2 | 359 | °C | TGA |
| Brittleness Temperature | < -50.0 | °C | ASTM D746A |
| Glass Transition Temperature | 70.0 | °C | DMA |
| Melting Temperature | 200 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 180 | °C | ASTM D3418 |
| Thermal Conductivity (23°C) | 0.79 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C, 3.20 mm) | 14 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 2.57 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index | > 52 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 8.0 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y1200 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Chemlon® MDF863 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Hanwha Total PP NH54I | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Jam HDPE HM9455F | Jam Petrochemical Company | HDPE | Jam HDPE |
| LNP™ THERMOCOMP™ AF006 compound | SABIC Innovative Plastics Europe | ABS | LNP™ THERMOCOMP™ |