NOVAPOL® PF-Y821 Series

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	NOVA Chemicals
Trademark:	NOVAPOL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	aXYbVs_NOVAPOL-PF-Y821-Series.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PF-Y821-BP:

Additives: 1000 ppm Slip, 3150 ppm Antiblock

Applications: General purpose packaging, bags requiring moderate clarity, bread bags.

PF-Y821-CP:

Additives: 2500 ppm Antiblock

Applications: Industrial packaging, heavy duty sacks

General Information
Additive	Processing aid Anti-caking agent (3150 ppm) [PF-Y821-BP] Anti-caking agent (2500 ppm) [PF-Y821-CP] Antioxidation Sliding agent (1000 ppm) [PF-Y821-BP]
Features	Butene comonomer Rigid, good smoothness Anti-caking property Antioxidation Machinable Compliance of Food Exposure Medium transparency
Uses	Packaging Bags Industrial application General Heavy packing bag
Agency Ratings	FDA 21 CFR 177.1520(c) 3.2a
Processing Method	Film extrusion Blow film

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.921	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.80	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
secant modulus			ASTM D882
1% secant, MD : 25 µm, blown film	210	MPa	ASTM D882
1% secant, TD : 25 µm, blown film	230	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield, 25 µm, blown film	10.0	MPa	ASTM D882
TD : Yield, 25 µm, blown film	11.0	MPa	ASTM D882
MD : Broken, 25 µm, blown film	45.0	MPa	ASTM D882
TD : Broken, 25 µm, blown film	33.0	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Broken, 25 µm, blown film	610	%	ASTM D882
TD : Broken, 25 µm, blown film	870	%	ASTM D882
Dart Drop Impact ¹(25 µm, Blown Film)	110	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, blown film	100	g	ASTM D1922
TD : 25 µm, blown film	400	g	ASTM D1922

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 25.0 µm, Blown Film)	57		ASTM D2457
Haze (25.0 µm, Blown Film)	12	%	ASTM D1003

Additional Information	Nominal Value	Unit	Test Method
Low Friction Puncture ²(25.0 µm)	320	J/cm	Internal method
Film properties are typical of blown film extruded on a 2.5" extruder with 4" die and 35-mil die gap at a blow up ratio of 2.5:1, but are dependent upon operating conditions.

Note Message
1 .	F50
2 .	Blown Film

Resin Grade	Manufacturer	Category	Trademark
Sevrene® 4500-70A	Vi-Chem Corporation	TPE	Sevrene®
Stanyl® 46HF5041LW	DSM Engineering Plastics	Nylon 46	Stanyl®
GAPEX® HT RNP33LB01BK	Ferro Corporation	Nylon+PP	GAPEX® HT
GS Pla® GZ95T	Mitsubishi Chemical Performance Polymers, Inc.	Biodeg Polymers	GS Pla®
Sylvin 9915-90 Blue 8364	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin