ACCUCOMP™ ACE092L
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aXIwQK_ACCUCOMP-ACE092L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUCOMP™ ACE092L is an Acetal (POM) Copolymer product. It is available in North America. Primary characteristic: medium viscosity. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 2650 | MPa | ASTM D790 |
| Flexural Strength | 92.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 65 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 158 | °C | |
| 1.8 MPa, Unannealed | 110 | °C | |
| Melting Temperature | 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-17G | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Rhelon G1050H-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| Adiprene® LW 520 | Chemtura | PUR-Eth,aliphat | Adiprene® |
| GATONE™ 5300X | Solvay Specialities India Private Limited (SSIPL) | PEEK | GATONE™ |
| Karina WHITE PVC COMPOUND 550-10/10-IS-SD-AS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |