ElectriPlast® EP-CF/ABS
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Integral Technologies, Inc. |
| Trademark: | ElectriPlast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aWsXAU_ElectriPlast-EP-CF-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ElectriPlast®EP-CF/ABS is an acrylonitrile butadiene styrene (ABS) product, which contains nickel-plated carbon fiber. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7100 | MPa | ASTM D638 |
| Tensile Strength (Break) | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 6030 | MPa | ASTM D790 |
| Flexural Strength | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 51 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 96.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | ESD STM11.11 |
| Volume Resistivity | 21 | ohms·cm | ASTM D257 |
| Static Decay | 10 | msec | Internal method |
| Surface Resistance | 10 | ohms | ESD STM11.11 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 29 | mm/min | UL 94 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 252 | °C | |
| Middle Temperature | 257 | °C | |
| Front Temperature | 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 37.8 | °C | |
| Back Pressure | 2.21 | MPa | |
| Screw Speed | 125 | rpm |
| Injection instructions |
|---|
| Injection Speed: 1 in/sec1st Stage (injection): 2400 psi2nd Stage (molding): 400 psiDecomposition: 0.5 inch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFILL H 15 20 T0 | RIALTI Srl | PP Homopolymer | RIALFILL |
| XT® Polymer 250 | Evonik Cyro LLC | Acrylic (PMMA) | XT® Polymer |
| Nycast Nyloil-MDX | Cast Nylons Ltd. | Nylon 6 | Nycast |
| Elastron® G G601.A85.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Plexiglas® Q | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |