SABIC® LDPE 2004TX37
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aWnXQC_SABIC-LDPE-2004TX37.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC®LDPE 2004TX37 is a low density polyethylene product,. It can be processed by blowing film and is available in Europe. SABIC®The application areas of LDPE 2004TX37 include packaging, film and food contact applications. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.7 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm, blown film | 190 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 190 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, blown film | 12.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : 25 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 15.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 25 µm, blown film | 100 | % | ISO 527-3 |
| TD : Broken, 25 µm, blown film | > 450 | % | ISO 527-3 |
| Total Energy Impact (25 µm, Blown Film) | 0.375 | J | ASTM D4272 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 25 µm, blown film | 2.0 | N | ISO 6383-2 |
| TD : 25 µm, blown film | 0.75 | N | ISO 6383-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 53 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 9.5 | % | ASTM D1003 |
| Additional Information |
|---|
| 25µm blown film processed with a blow up ratio of 3:1 and a die gap of 0.8 mm.Clarity, SABIC Method, Blown Film, 25µm: 23mVBlocking, SABIC Method, Blown Film: <5gRe-blocking, SABIC Method, Blown Film: 100g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 37W300 | AD majoris | PBT | MALAT |
| Sylvin 8245-50 White 1484 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CYCOLAC™ INP562 resin | SABIC Innovative Plastics | ABS+SAN | CYCOLAC™ |
| Infino NH-1015V | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |
| LUVOCOM® 1105-7670/BL | Lehmann & Voss & Co. | PEEK | LUVOCOM® |