Next Nylon 66 Prime Series PG40-01BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aWCrgo_Next-Nylon-66-Prime-Series-PG40-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced Black Compound Product Applications This grade is widely used for Automotive parts - pedal oil filter housing, clutch master cylinder etc Benefits offering Excellent combination of thermal stability and Mechanical properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.46 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.20 | -- | % | ASTM D955 |
| Transverse flow | 0.45 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.7 | -- | % | ASTM D570 |
| Saturation 1 | 5.8 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 105 | -- | ASTM D785 | |
| Class r | 125 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 200 | 160 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 6.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | 6500 | MPa | ASTM D790 |
| Flexural Strength | 285 | 220 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 160 | 190 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 260 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 254 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+16 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 27 | 24 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | > 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 290 | °C | |
| Front Temperature | 290 - 300 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ GA520 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| SLOVALEN® PC 81 T 15 | Plastcom | PP, Unspecified | SLOVALEN® |
| Cheng Yu FR200GV25 | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| DINALON® B1S25 G30-0008 | Grupo Repol | Nylon 6 | DINALON® |
| Plasmer 5050D-1/3839 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |