Niretan A F30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niretan A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aVfGEk_Niretan-A-F30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyammide 66 reinfirced with 30% glass fibre, for the injection moulding of items requiring, a good aesthetical surface. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 7.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | 90 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1(Break) | 160 | 110 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.5 | 4.5 | % | ASTM D638 |
| Flexural Modulus 3 | 8500 | 6000 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 250 | 160 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -20°C, 3.20 mm | 60 | 100 | J/m | |
| 23°C, 3.20 mm | 80 | 130 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | -- | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 260 | -- | °C | ASTM D3418 |
| CLTE - Flow | 3.0E-6 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 30 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® SJ5400 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Shin-Etsu Elastomer KE-9510U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| SILVER® PC230 | Guangdong Silver Age Sci & Tech. Co., Ltd | PC | SILVER® |
| Colorite G Series 10013G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| Hyrene® PSCRY 2.5 | Entec Polymers | PS (GPPS) | Hyrene® |