Mylar® A (92 guage)
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | DuPont Teijin Films U.S. |
| Trademark: | Mylar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aU6pI0_Mylar-A-92-guage-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mylar Type A films have balanced tensile properties and excellent resistance to moisture and most chemicals. They can withstand temperature extremes from -94 to 302°F. Mylar does not become brittle with age under normal conditions, because it contains no plasticizers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ASTM D1505 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 0.0230 mm | 1.9 | % | |
| Across Flow : 0.0230 mm | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Poisson's Ratio | 0.38 | ASTM E132 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 4900 | MPa | |
| 1% Secant, TD | 5100 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break | 193 | MPa | |
| TD : Break | 234 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 110 | % | |
| TD : Break | 90 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 254 | °C | |
| CLTE - Flow | 1.7E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1170 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.15 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength | 280 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.20 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | VTM-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 16 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y600 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Toraycon® 1401X31 | Toray Resin Company | PBT | Toraycon® |
| Adiprene® LF 1600D | Chemtura | PUR-Ester/TDI | Adiprene® |
| ATTANE™ SL 4102G | The Dow Chemical Company | ULDPE | ATTANE™ |
| Sumiliteresin® PR-2400 I | SBHPP | Phenolic | Sumiliteresin® |