Witcom PPS 8G/3L1
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aTm4ul_Witcom-PPS-8G-3L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PPS 8G/3L1 is a branched polyphenylene sulfide product, which contains a 40% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.77 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 - 0.40 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.030 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 - 2.0 | % | ISO 527-2 |
| Flexural Modulus | 13000 | MPa | ISO 178 |
| Flexural Stress | 215 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 8.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| CLTE - Flow | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 200 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 160 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 305 - 345 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOCOMP® PA66 CF30 TS7 | EPIC Polymers | Nylon 66 | TRIBOCOMP® |
| Nycal™ 1850T1H | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| Grilon® TSG-30/4 LF 15/1 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| PLASTRON™ PAX-GF50-02 | Daicel Polymer Ltd. | Nylon, Unspecified | PLASTRON™ |
| Sumiliteresin® PR-1051 I | SBHPP | Phenolic | Sumiliteresin® |