SABIC® LLDPE 430BE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aSDTk3_SABIC-LLDPE-430BE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 430BE is a butene linear low density polyethylene resin. The material, natural resin, is typically used for cast film applications, offering good mechanically properties, stiffness enhancement and furthermore enables to gain high line speeds. SABIC® LLDPE 430BE is provided with a dedicated anti oxidant package suitable for cast film extrusion with low gel levels. Applications Skin layers for non-cling stretch cast film, cast film side encapsulation, mid layer hygienic cast film and product to realize downgauging by stiffness enhancement. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.2 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Elastic Recovery - Cast Film (20.0 µm) | 45 | % | ASTM D5459 |
| Protrusion Puncture Resistance - Cast Film (20.0 µm) | 0.500 | J | ASTM D5748 |
| Stress Retention - Cast Film (20.0 µm) | 78 | % | ASTM D5459 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Impact - Cast Film (20.0 µm) | 15.0 | J/cm | ISO 7765-2 |
| Tear Strength - TD 1(20.0 µm) | 117.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 109 | °C | ISO 306/A |
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 91 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 2.4 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Properties are determined on 20 µm cast stretch film produced on a 2 m commercial cast stretch line: melt temperature 270°C, chill roll temperature 20°C and line speed of 450 m/min. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 - 300 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil SFM5-2350 | NuSil Technology | Silicone | NuSil |
| BESTNYL SE25VI01AX-1 | Triesa Plastics | Nylon 66 | BESTNYL |
| Caltex PP MT62CS | GS Caltex | PP, Unspecified | Caltex PP |
| Hifax TYC 900P | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Lucent PC PC/PBT-1230 | Lucent Polymers, Inc. | PC+PBT | Lucent PC |