| TORZEN® HV125A NC01 is a high viscosity PA66 resin for extrusion and injection molding applications. It is non-lubricated. Available in natural and black. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow : 2.00mm | 1.7 | % | ISO 294-4 |
| Flow : 2.00mm | 1.7 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.8 | % | ISO 62 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 230 | cm³/g | ISO 307 |
| Relative Viscosity | |||
| at 1% in sulfuric acid, nominal | 4 | ||
| in formic acid, nominal | 125 | ASTM D789 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.3 | % | ISO 527-2 |
| Fracture | 50 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 2.3 | kJ/m² | ISO 179 |
| 23°C | 5.2 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ISO 179 | |
| 23°C | No Break | ISO 179 | |
| Notched Izod Impact (23°C) | 4.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 202 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 68.0 | °C | ISO 75-2/A |
| Melting Temperature | 263 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (2.00 mm) | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 10 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | > 600 | V | ASTM D3638 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.010 - 0.080 | % | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Back Pressure | 0.200 - 1.00 | MPa | |
| Screw Speed | 75 - 180 | rpm | |
| Cushion | 4.00 - 6.00 | mm | |
| Vent Depth | 7.0E-3 - 0.040 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XAREC™ SP140 | Idemitsu Kosan Co., Ltd. | SPS | XAREC™ |
| ACCUTECH™ HP0339T30L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Iupital® TC3015 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| Polifor® E 16 TR/10 NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
| Durethan® BM 25 FN20 700350 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |