Huafon JF-P-4170T / JF-I-4118 (midsole)
| Category: | PUR-Ester , Polyurethane (Polyester based) |
| Manufacturer: | Huafon Group Co., Ltd. |
| Trademark: | Huafon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aRYmsU_Huafon-JF-P-4170T-JF-I-4118-midsole-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characteristic: Low hardness and high density. Application: For casual shoes and direct injection shoes. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density 1 | 0.550 to 0.600 | g/cm³ |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Hardness | |||
| Asker A : 23°C | 45.0 to 50.0 | ||
| Asker C : 23°C | 60.0 to 65.0 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 90 to 92 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color 2 | Clear/Transparent | ||
| Density | |||
| 40°C 3 | 1.17 to 1.19 | g/cm³ | |
| 40°C 4 | 1.18 to 1.20 | g/cm³ | |
| Viscosity | |||
| 40°C 5 | 0.20 to 0.50 | Pa·s | |
| 40°C 6 | 0.80 to 1.2 | Pa·s |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | > 5.00 | MPa | |
| Tensile Elongation at Break | > 450 | % | |
| Tear Strength | > 20.0 | kN/m |
| Note Message | |
|---|---|
| 1 . | Molded Density |
| 2 . | Part B |
| 3 . | Part A |
| 4 . | Part B |
| 5 . | Part B |
| 6 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1500-55D | RTP Company | TEEE | RTP |
| POLYPRO® 5030 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| ADENE® M38VQEGD00 | A.D. Compound S.p.A. | PP Copolymer | ADENE® |
| Sumiliteresin® PR-55386 I | SBHPP | Phenolic | Sumiliteresin® |
| LUVOCOM® 1105-8292 VP | LEHVOSS Group | PEEK | LUVOCOM® |