Arnitel® PL461
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnitel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aR0637_Arnitel-PL461.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arnitel® PL461 is a Thermoplastic Copolyester Elastomer (TPC-ET) material. It is available in Asia Pacific, Europe, or North America for injection molding. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 39.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.8 | % | |
| Flow | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 45 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 135 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 21.0 | MPa | |
| 5.0% Strain | 6.00 | MPa | |
| 10% Strain | 9.20 | MPa | |
| 50% Strain | 13.2 | MPa | |
| 100% Strain | 14.4 | MPa | |
| Nominal Tensile Strain at Break | 350 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 65.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 189 | °C | ISO 306/A50 |
| Melting Temperature 1 | 220 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® DR | Röchling Engineering Plastics SE & Co. KG | HMWPE | POLYSTONE® |
| POLYSTONE® G black B | Röchling Engineering Plastics SE & Co. KG | HDPE | POLYSTONE® |
| Cri-Line LC-915-THK | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| INEOS PP H02G-02 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| Karina BLACK PVC COMPOUND 550-48/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |