Bayblend® FR3030
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aQUBFZ_Bayblend-FR3030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+ABS) blend; unreinforced; flame-retardant; extrusion grade; Vicat/B 120 temperature = 115 °C; good extrusion and vacuum-forming behaviour; UL recognition 94 V-0 (1.5 mm); halogen-free according to DIN VDE 0472,815; glow wire temperature (GWFI): 960 °C at 1.0 mm. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 260°C, 3.00 mm | 0.50 to 0.70 | % | |
| Flow : 260°C, 3.00 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2650 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 69.0 | MPa | |
| Break, 23°C | 53.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 5.0 | % | |
| Break, 23°C | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 106 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 98.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 113 | °C | ISO 306/B50 |
| -- | 115 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 6.8E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.20 | ||
| 23°C, 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 3.7E-3 | ||
| 23°C, 1 MHz | 7.5E-3 | ||
| Comparative Tracking Index (Solution A) | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| 3.00 mm | 5VA |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 2(260°C) | 410 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm, 80°C MT |
| 2 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ LC30 | Mando Advanced Materials Co., Ltd. | PP Copolymer | SEPAZ™ |
| Ultradur® B 4406 | BASF Corporation | PBT | Ultradur® |
| Baoding 65E85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| ELIX™ ABS P3H-AT | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| KMI PC 121LB | KMI Group Inc. | PC | KMI PC |